305 Stainless Steel Bar Rod manufacturer

Type 305 is a chromium nickel austenitic stainless steel with a low rate of work hardening due to the elevated nickel content. This low rate of work hardening makes this grade well suited for multi-stage deep drawing applications without process annealing where 304/304L may suffer from cracking issues. Type 305 is non-magnetic in the annealed and cold worked conditions and has corrosion resistance similar to 304/304L stainless steel.

305 Stainless Steel Bar Rod Price in China ,Manufacturer of 304 Stainless Steel Bar Rod

305 Stainless Steel is an austenitic chromium nickel stainless steel with a low rate of work hardening. This low rate of work hardening makes it suitable for many deep drawing applications. In order to minimize earring during drawing, the directionality introduced during cold rolling must be kept to a minimum amount. Deep drawing quality should be noted when ordering this alloy. Ordering annealed or dead soft does not guarantee deep drawing quality. Type 305 is non magnetic and becomes magnetic ( at a slow rate) with increasing cold work.

 The 305 Stainless Steel  Bar is used mostly for its high geometrical strength. The applications include construction and other commercial applications as well. The strength, heat resistance and corrosion resistance are all the result of the composition. The material includes carbon, manganese, phosphorus, silicon, sulfur and chromium and nickel. Please contact us for more information on the SS 305  Bar and other types as well as their pricing.

Click to Request Information >

Equivalent Material of 305 Stainless Steel Bar Rod

Grade UNS No. Old British Euronorm China GB Japanese JIS
BS EN No. Name
305 S30500 / / / 12CrNi3A 1Cr18Ni12 SUS305

Standard Specification Of ASTM A240 Type 305 Stainless Steel Bar Rod

Specifications ASTM A240
Diameter 3、5、6、7、8、9、10、12、15、18、20、25、30、35、40、50、100、200etc
Length 2000mm, 2500mm, 3000mm,3500mm, 4000mm 5000mm 6000mm 10000mm 12000mm etc
Surface Black 、 bright、 pickling 、etc
Finish Hot rolled plate (HR), Cold rolled sheet (CR), 
Form Rod, Round, Channel Bar, Rings, Round Rod, Triangle, Hollow, Rectangle, T-Bar, Flat Bar, Precision Ground Bar, Blocks, Square, Threaded, Hex (A/F), Profiles, Half Round Bar, Ingot, Billet, I/H Bar, Forging etc.

305 Stainless Steel Bar Rod Composition and Mechanical Characteristics

Grade C Mn Si P S Cr Mo Ni N
305 Min.
Max.
/
0.12
/
2.0
/
1.0
/
0.045
/
0.030
18.00
/
/ 12.00
/
/
Grade Tensile Strength
(MPa) 
Yield Strength
0.2% Proof (MPa) 
Elongation
(% in 50mm)
Hardness
Rockwell B
(HR B)
Brinell
(HB)
305 585 260 40   88

Common Types Of 305 Stainless Steel Bar Rod

  • 305 Stainless Steel Bar Rod

  • 305 Stainless Steel Bar Rod

  • 305 Stainless Steel Bar Rod

Dimensions Standard,weight chart and size schedules of 305 Stainless Steel Bar Rod

SS 305 rod Diameter Weight chart per meter SS 305 rod Diameter Weight chart per meter
3mm 0.06 Kg 1/8'' 0.06 kg
4mm 0.10 Kg 3/16'' 0.14 kg
5mm 0.16 Kg 1/4'' 0.25 kg
6mm 0.22 Kg 5/16'' 0.39 kg
7mm 0.30 Kg 3/8'' 0.56 kg
8mm 0.40 Kg 7/16'' 0.77 kg
10mm 0.62 Kg 1/2'' 1.00 kg
12mm 0.89 Kg 9/16'' 1.22 kg
14mm 1.22 Kg 5/8'' 1.56 kg
15mm 1.40 Kg 11/16'' 1.89 kg
16mm 1.59 Kg 3/4'' 2.25 kg
18mm 2.01 Kg 7/8'' 3.07 kg
20mm 2.48 Kg 1'' 4.03 kg
22mm 3.00 Kg    
24mm 3.57 Kg    
25mm 3.88 Kg    

Price list

305 Stainless Steel Bar Rod Price List 304L Stainless Steel Bar Rod FOB Shanghai Per Unit (USD)
305 stainless steel black rod $1500.00-$2000.00
305 stainless steel bright rod $1800.00-$2300.00
305 stainless steel pickling rod $1500.00-$2000.00

CONTACT US

top